Description
LOW CARBON WIRE HOT DIPPED
Hot dip galvanizing means the immersion of Low carbon wire in a molten zinc tank at a temperature of 450 ° C which causes the wire to be covered with a thin and resistant layer of zinc
UNI EN10244-2:2003 EN10257-1 Tab 1 EN10257 Tab 2
Example Table:
DIA. mm. |
TS N/mm2 |
TOLL. | Q.Zinc Gr/m2 mm. |
EL.%. |
---|---|---|---|---|
0.20 | 330-430 | +-0.015 | 28-35 min | >15% |
0.24 | 330-430 | +-0.015 | 28-35 min | >15% |
0.30 | 330-430 | +-0.020 | 28-35 min | >15% |
0.35 | 330-430 | +-0.020 | 28-35 min | >15% |
0.40 | 300-400 | +-0.020 | 28-35 min | >15% |
0.50 | 300-400 | +-0.020 | 28-35 min | >15% |
0.60 | 300-400 | +-0.020 | 28-35 min | >15% |
0.70 | 300-400 | +-0.020 | 28-35 min | >15% |
0.80 | 300-400 | +-0.020 | 28-35 min | >15% |
0.90 | 300-400 | +-0.020 | 28-35 min | >15% |
1.00 | 300-400 | +-0.020 | 28-35 min | >15% |
1.10 | 300-400 | +-0.020 | 28-35 min | >15% |
1.20 | 300-400 | +-0.020 | 28-35 min | >15% |
APPLICATION: Braiding, Knitting, Weaving, , Mesh, other applicationS
PACKING – SPOOLS